AbstractErosion of limiters, walls and divertor plates is likely to be a serious concern in the next generation of fusion devices. The main mechanisms of erosion are reviewed and the spatial distribution of erosion and deposition are discussed. Measurements of erosion and redeposition have been made at the JET limiters under different conditions and net erosion in the range 10–100 μum detected after typically 3000 10 s discharges. Modelling of the distribution is in quite good agreement with the experimental data and net to gross erosion ratios of 0.2 to 0.3 are calculated.The problem of extrapolating to reactor conditions is discussed. While there are serious difficulties in carrying out this extrapolation, the higher edge densities envisaged should lead to lower ratios of net to gross erosion than in present experiments.
次世代核融合装置において、リミター、壁、およびダイバータ板の侵食は深刻な問題となる可能性が高い。侵食の主なメカニズムを概説し、侵食と再堆積の空間分布について考察する。JETリミターにおいて異なる条件下で侵食と再堆積の測定が行われ、典型的には3000回の10秒放電後に10〜100μmの範囲の正味侵食が検出された。分布のモデル化は実験データとかなり良く一致しており、正味侵食と総侵食の比は0.2〜0.3と計算される。炉条件への外挿の問題について考察する。この外挿を実施するには深刻な困難があるものの、想定されるより高い周辺密度は、現在の実験よりも低い正味侵食と総侵食の比をもたらすはずである。