AbstractImpurity of SiCf/SiC composites prepared by CVI was analyzed by neutron activation analysis and glow discharge mass spectrometry. The evaluation of the induced activity of the composites based on the chemical compositions was made using a simulation calculation for fusion reactor blanket. Impurities of 35 elements were detected in the composites. However, the total concentration of metallic impurities was below 20 mass ppm. The analyses of induced activity of the composites show that the dose rate decreases by about six orders of magnitude in a day after the shutdown. It is recommended that the purification of SiC composites, especially reduction of Fe and Ni contents, is necessary to reduce the activity to satisfy the limit of remote handling recycling after several 10 years cooling of fusion reactors.
CVI法により作製したSiC/SiC複合材料の不純物を、中性子放射化分析およびグロー放電質量分析により分析した。化学組成に基づく複合材料の誘導放射能の評価は、核融合炉ブランケットに対するシミュレーション計算を用いて行った。複合材料中には35元素の不純物が検出された。しかしながら、金属不純物の総濃度は20質量ppm未満であった。複合材料の誘導放射能の分析により、線量率は停止後1日で約6桁減少することが示された。核融合炉の数十年間の冷却後に遠隔操作による再循環の制限を満たすために放射能を低減するには、SiC複合材料の精製、特にFeおよびNi含有量の低減が必要であることが推奨される。