AbstractCompression properties of neutron irradiated beryllium pebbles manufactured by the rotating electrode method and the Mg reduction method were evaluated from compression load tests at 10% deformation. Neutron irradiation was carried out up to a total fast neutron fluence of about 4×1025 n/m2 (E>1 MeV, about 8 dpa) at 400, 500 and 600°C. There was no significant difference for the two kinds of beryllium pebbles. Additionally, it became clear that not only helium concentration, but also dpa value is an important factor which might influence the compression properties, because the compression load at 10% deformation for the present specimens irradiated at high dpa was smaller than that of the specimens, with similar helium concentration, irradiated at low dpa.
中性子照射されたベリリウムペブルの圧縮特性を、10%変形時の圧縮荷重試験から評価した。ベリリウムペブルは回転電極法およびMg還元法により製造された。中性子照射は、400、500、600°Cにおいて、全中性子フルエンス約4×10²⁵ n/m²（E>1 MeV、約8 dpa）まで実施した。2種類のベリリウムペブル間で有意な差は認められなかった。さらに、高dpaで照射された本試験片の10%変形時の圧縮荷重は、同様のヘリウム濃度を有する低dpaで照射された試験片よりも小さかったことから、圧縮特性に影響を及ぼす可能性のある因子として、ヘリウム濃度だけでなくdpa値も重要であることが明らかになった。