Sorption and desorption behavior of hydrogen isotopes from tungsten deposits caused by deuterium gas or deuterium plasma exposure

Shinichiro Ishikawa, Kazunari Katayama, Yasuhito Ohnishi, Satoshi Fukada, Masabumi Nishikawa2012年Fusion Engineering and DesignIF 1.7 出版社

wiki

Tungsten Deuterium Hydrogen isotopes Deuterium plasma

この論文にはまだAI要約がありません。

関連論文

Stabilization of defects by the presence of hydrogen in tungsten: simultaneous W-ion damaging and D-atom exposure

2019Nuclear Fusion

Surface modification and deuterium retention in rhenium doped tungsten exposed to low energy deuterium plasma

2021Fusion Engineering and Design

Deuterium retention in tungsten oxide: the role of oxide damage

2025Nuclear Fusion

Deuterium release from deuterium plasma-exposed neutron-irradiated and non-neutron-irradiated tungsten samples during annealing

2020Nuclear Fusion

Hydrogen incorporation in tungsten deposits growing by deuterium plasma sputtering

2011Fusion Engineering and Design

Energy confinement of hydrogen and deuterium H-mode plasmas in JT-60U

2012Nuclear Fusion

Aggravated blistering and increased deuterium retention in iron-damaged tungsten after exposure to deuterium plasma with various surface temperatures

2018Nuclear Fusion

Review of hydrogen isotope effects on H-mode confinement in JT-60U

2021Plasma Physics and Controlled Fusion

Temperature dependence of blistering and deuterium retention in tungsten exposed to high-flux and low-energy deuterium plasma

2008Fusion Engineering and Design

Deuterium retention in carbon flakes and tungsten–carbon mixed flakes produced by deuterium arc discharge

2005Nuclear Fusion