AbstractA concrete assembly was irradiated by D-T neutrons for 10 h, and dose rate measurement one day after shutdown has been carried out in order to provide a guide line for selection studies of low activation concrete. The experimental results were analyzed by the two dimensional calculation code DOT3.5 with its related nuclear data library GICX40 based on ENDF/B-III, however disagreement between experiment and calculation was observed in the deeper detector positions. Calculations were also performed using the nuclear data library based on ENDF/B-IV, and agreement within experimental errors was obtained at all detector positions. Selection studies for low activation concrete were performed using this nuclear data library. As a result, it was found that limestone concrete exhibited excellent properties as a low activation concrete in fusion facilities.
コンクリート供試体をD-T中性子により10時間照射し、その1日後の線量率測定を、低放射化コンクリートの選定研究のための指針を得る目的で実施した。実験結果は、ENDF/B-IIIに基づく関連核データライブラリGICX40を用いた二次元計算コードDOT3.5により解析したが、より深い検出器位置において実験と計算の間に不一致が観察された。また、ENDF/B-IVに基づく核データライブラリを用いた計算も実施し、全ての検出器位置において実験誤差内での一致が得られた。この核データライブラリを用いて、低放射化コンクリートの選定研究を実施した。その結果、石灰岩コンクリートが核融合施設における低放射化コンクリートとして優れた特性を示すことが判明した。