A support laboratory has been set up to study pellet production, launch and shattering of cryogenic protium, deuterium, and neon pellets for the ITER disruption mitigation system, which plans to use 28.5 × 57 mm (diameter × length) protium, neon an mixture pellets in the Shattered Pellet Injectors. Such large protium pellets have not been produced and launched before, therefore the desublimation and launch process have been studied in detail in two steps. First 19 mm diameter pellets were produced, followed by the demonstration of the final pellet size. Pellet desublimation recipes were established for all pellet types, and it was found that, under certain conditions, even the large neon pellets can be launched with a propellant gas pulse, without requiring a mechanical punch device. This is attributed to cryogenic snow formation on the surface of the pellet. Conditions for the snow formation are studied and tendencies are understood using simple calculations.
核融合実験炉ITERの擾乱緩和システム用の極低温プロチウム、重水素、ネオンペレットの製造、発射、破砕を研究するために支援実験室が設置された。このシステムは、破砕ペレット入射装置において28.5×57 mm（直径×長さ）のプロチウム、ネオンおよび混合ペレットを使用する計画である。このような大型のプロチウムペレットはこれまで製造・発射されたことがないため、脱昇華および発射プロセスを2段階に分けて詳細に研究した。最初に直径19 mmのペレットを製造し、続いて最終ペレットサイズの実証を行った。すべてのペレットタイプについてペレット脱昇華レシピを確立し、特定の条件下では、機械的な打ち出し装置を必要とせずに、推進ガスパルスによって大型ネオンペレットでさえ発射できることが判明した。これはペレット表面での極低温スノー生成に起因する。スノー生成の条件を研究し、その傾向を簡単な計算を用いて理解した。