This study focuses on the removal of trapped D from thick codeposits on JET divertor tiles via thermo-oxidation. The tiles were removed from the JET Mark II Gas Box divertor after the 1998–2001 campaign. These codeposits have Be concentrations of up to ∼60% Be/(Be + C) and their thicknesses range from 10 to 270 µm. Laser thermal desorption spectroscopy was used to determine the D removal rates and final remaining D concentrations following oxidation. Estimates of the carbon removed during oxidation were obtained from mass-loss measurements. The initial rate of D removal was found to be much higher for the thick codeposits of this study than for the previously studied codeposits with thicknesses in the range 1–5 µm (from TFTR, DIII-D and JET). This is despite the large Be concentrations. For oxidation performed at 623 K (350 °C) and 21 kPa (160 Torr) O2 pressure the initial D removal rates were found to increase linearly with increasing 'inherent' D content; about 50% of the inherent D was removed from all specimens in the first 15 min—independent of Be content and codeposit thickness. Following 8 h of oxidation, the fraction of D removed was >85% for all specimens, again, independent of Be content and thickness.
本研究は、JETダイバータタイル上の厚い共堆積物からの熱酸化による捕捉重水素（D）の除去に焦点を当てたものである。タイルは1998年から2001年のキャンペーン後にJET Mark II Gas Boxダイバータから取り外されたものである。これらの共堆積物は、最大約60%のBe/(Be+C)濃度を有し、厚さは10〜270 µmの範囲である。レーザー熱脱離分光法を用いて、酸化処理後のD除去率と残留D濃度を測定した。酸化中に除去された炭素の量は、質量損失測定から推定された。本研究の厚い共堆積物におけるDの初期除去率は、以前に研究された厚さ1〜5 µmの共堆積物（TFTR、DIII-D、JET由来）のそれよりもはるかに高いことが判明した。これは、高いBe濃度にもかかわらずである。623 K（350°C）および21 kPa（160 Torr）のO₂圧力で酸化を行った場合、Dの初期除去率は、初期D含有量の増加に伴って直線的に増加することが見出された。全試料において、最初の15分間で初期Dの約50%が除去されたが、これはBe濃度や共堆積物の厚さに依存しなかった。8時間の酸化後には、全試料でDの除去率は85%を超え、これもまたBe濃度や厚さに依存しなかった。