Cracking and grain refining behaviors of tungsten based plasma facing materials under fusion relevant transient heat flux

Xiangbin Li, Dahuan Zhu, Changjun Li, Junling Chen2017年Fusion Engineering and DesignIF 1.7 出版社

wiki

Tungsten Plasma-facing component

この論文にはまだAI要約がありません。

関連論文

Baseline high heat flux and plasma facing materials for fusion

2017Nuclear Fusion

Influence of porosity and blistering on the thermal fatigue behavior of tungsten

2022Nuclear Fusion

Development of advanced high heat flux and plasma-facing materials

2017Nuclear Fusion

Recrystallization-mediated crack initiation in tungsten under simultaneous high-flux hydrogen plasma loads and high-cycle transient heating

2021Nuclear Fusion

Characterization of in situ damage to tungsten PFCs induced by transient heat flux during plasma disruption in EAST

2025Nuclear Fusion

Behaviour of melted tungsten plasma facing components under ITER-like transient heat loads: Simulations and experiments

2008Fusion Engineering and Design

High heat flux test on first wall materials

1991Fusion Engineering and Design

The impact of transient heat flux on tungsten fiber-reinforced tungsten materials

2026Fusion Engineering and Design

Coupled interactions between tungsten surfaces and transient high-heat-flux deuterium plasmas

2015Nuclear Fusion

Fracture behavior of tungsten-based composites exposed to steady-state/transient hydrogen plasma

2020Nuclear Fusion