Numerical analysis of deuterium migration behaviors in tungsten damaged by fast neutron by means of gas absorption method

Makoto I Kobayashi, Masashi Shimada, Chase N Taylor, Yuji Nobuta, Yasuhisa Oya2021年Fusion Engineering and DesignIF 1.7 出版社

wiki

Fusion Advanced Studies Torus Tungsten Deuterium

この論文にはまだAI要約がありません。

関連論文

Deuterium release from deuterium plasma-exposed neutron-irradiated and non-neutron-irradiated tungsten samples during annealing

2020Nuclear Fusion

Sorption and desorption behavior of hydrogen isotopes from tungsten deposits caused by deuterium gas or deuterium plasma exposure

2012Fusion Engineering and Design

On the reduction of deuterium retention in damaged Re-doped W

2013Nuclear Fusion

Approaching a deuterium quantitative determination methodology in tungsten matrices

2025Fusion Engineering and Design

Gas-driven permeation of deuterium through tungsten and tungsten alloys

2016Fusion Engineering and Design

Stabilization of defects by the presence of hydrogen in tungsten: simultaneous W-ion damaging and D-atom exposure

2019Nuclear Fusion

Depth-resolved deuterium retention analysis in displacement-damaged tungsten using laser-induced breakdown spectroscopy

2024Physics of Plasmas

The influence of displacement damage on deuterium retention in tungsten exposed to plasma

2009Nuclear Fusion

Deuterium trapping by irradiation damage in tungsten induced by different displacement processes

2013Fusion Engineering and Design

Study of deuterium retention on lithiated tungsten exposed to high-flux deuterium plasma using laser-induced breakdown spectroscopy

2014Fusion Engineering and Design