AbstractIn the frame of the European Technology R&D program for ITER, and in the area of High Heat Flux plasma facing Components (HHFC), representative small-scale mock-ups were manufactured and tested to compare different concepts and joining technologies (i.e. active brazing, Hot Isostatic Pressing (HIPping), diffusion bonding, etc.). On the basis of the results obtained by thermal fatigue tests, the monoblock concept resulted to be the most promising one, particularly when the HIPping manufacturing technology is used. Within this program, ENEA manufactured tungsten monoblock mock-ups by using the HIPping technology. The mock-ups were tested with respect to thermal fatigue and, upon screening tests, the best performance obtained was 15 MW/m2 for 200 cycles. One of these mock-ups was enclosed in the ‘Paride’ neutron irradiation campaign. This campaign has the scope of enlarging the available database on the performance degradation of prototypical basic solutions of the ITER plasma facing components due to neutron irradiation. The manufacturing procedure and the results of the screening and fatigue thermal tests performed on the ENEA mock-ups are reported in this paper.
欧州研究開発プログラムITERの枠組みにおいて、高熱流束プラズマ対向機器（HHFC）の分野では、異なる概念と接合技術（すなわち、活性ろう付け、熱間静水圧加圧（HIP）、拡散接合など）を比較するために、代表的な小型モックアップが製作され、試験が実施された。熱疲労試験の結果に基づき、モノブロック概念が最も有望であると判断された。特に、HIP製造技術を用いた場合にその優位性が顕著であった。本プログラムにおいて、ENEAはタングステンモノブロックモックアップをHIP技術を用いて製作した。モックアップは熱疲労に関して試験され、スクリーニング試験の結果、最良の性能は15 MW/m²で200サイクルであった。これらのモックアップの1つは、「Paride」中性子照射キャンペーンに組み込まれた。このキャンペーンは、ITERのプラズマ対向機器の原型的基本ソリューションにおける、中性子照射による性能劣化に関する既存のデータベースを拡大することを目的としている。本論文では、ENEAモックアップの製造手順と、実施されたスクリーニング試験および熱疲労試験の結果について報告する。