Tungsten-coated tiles, manufactured by plasma spray on graphite, were mounted in the divertor of the ASDEX Upgrade tokamak and cover almost 90% of the surface facing the plasma in the strike zone. Over 600 plasma discharges have been performed to date, around 300 of which were auxiliary heated with heating powers up to 10 MW. The production of tungsten in the divertor was monitored by a W I line at 400.8 nm. In the plasma centre an array of spectral lines at 5 nm emitted by ionization states around W XXX was measured. From the intensity of these lines the W content was derived. Under normal discharge conditions W-concentrations around or even lower were found. The influence on the main plasma parameters was found to be negligible. The maximum concentrations observed decrease with increasing heating power. In several low power discharges accumulation of tungsten occurred and the temperature profile was flattened. The concentrations of the intrinsic impurities carbon and oxygen were comparable to the discharges with the graphite divertor. Furthermore, the density and the limits remained unchanged and no negative influence on the energy confinement or on the H-mode threshold was found. Discharges with neon radiative cooling showed the same behaviour as in the graphite divertor case.
プラズマ溶射によってグラファイト上に製造されたタングステン被覆タイルが、ASDEX Upgradeトカマクのダイバータに取り付けられ、ストライクゾーンにおいてプラズマに面する表面の約90%を覆っている。これまでに600回以上のプラズマ放電が実施され、そのうち約300回は最大10 MWの加熱パワーによる補助加熱を伴うものであった。ダイバータにおけるタングステンの生成は、400.8 nmのW I線によって監視された。プラズマ中心部では、W XXX付近の電離状態から放出される5 nmのスペクトル線群が測定された。これらのスペクトル線の強度から、タングステン含有量が導出された。通常の放電条件下では、タングステン濃度は約またはそれ以下であることが見出された。主要なプラズマパラメータへの影響は無視できる程度であることが確認された。観測された最大濃度は、加熱パワーの増加とともに減少した。いくつかの低パワー放電ではタングステンの蓄積が発生し、温度分布が平坦化した。内在的不純物である炭素と酸素の濃度は、グラファイトダイバータを用いた放電と同等であった。さらに、密度および限界は変化せず、エネルギー閉じ込めやHモード閾値への悪影響は見られなかった。ネオン放射冷却を伴う放電は、グラファイトダイバータの場合と同様の挙動を示した。